Pearlcoat

TPU FOR MELT CALENDER, EXTRUSION AND COATING SOLUTION PROCESSING

The Pearlcoat TPU product range is a special linear polyurethane that is mainly used in the hot melt coating process on textile substrates. Processing by extrusion, calendering and PVC compounding is also possible.

  • Special TPU granules based on polyester, polycaprolactone polyester, polyether and co-polyether
  • For the melt calender coatings, calender coating of textiles, such as conveyor belts, belts, tarpaulins, shoe and automotive textiles, etc.
  • In powder form for sintering and paste coating of textiles and nonwovens

Product name

Description

Data sheet

Safety data sheet

Applications

Compounds, Coextrusion

Polymer

Thermoplastic Polyurethane

Processing

Extrusion and Calander

Chemical structure

Aromatic polycaprolactone

Hardness

70A

Density

1,16 g/cm³

Form of delivery

Granules

Softening range

40 °C

Elongation at break

750 %

Tensile strength

20 MPa

Abrasion resistance

45 mm³

Applications

Coextrusion

Polymer

Thermoplastic Polyurethane

Processing

Extrusion and Calander

Chemical structure

Copolyester

Hardness

70A

Density

1,05 g/cm³

Form of delivery

Granules

Softening range

53 °C

Elongation at break

615 %

Tensile strength

30 MPa

Abrasion resistance

30 mm³

Applications

Conveyor belts

Polymer

Thermoplastic Polyurethane

Processing

Extrusion and Calander

Chemical structure

Aromatic polyesters

Hardness

85A

Density

1,20 g/cm³

Form of delivery

Granules

Elongation at break

5500 %

Tensile strength

30 MPa

Abrasion resistance

25 mm³

Applications

Conveyor belts, life jackets

Polymer

Thermoplastic Polyurethane

Processing

Extrusion and Calander

Chemical structure

Aromatic polyethers

Hardness

76A

Density

1,09 g/cm³

Form of delivery

Granules

Elongation at break

650 %

Tensile strength

25 MPa

Abrasion resistance

25 mm³

Applications

Conveyor belts

Polymer

Thermoplastic Polyurethane

Processing

Extrusion and Calander

Chemical structure

Aromatic polyethers

Hardness

82A

Density

1,11 g/cm³

Form of delivery

Granules

Elongation at break

550 %

Tensile strength

30 MPa

Abrasion resistance

25 mm³

Applications

Coextrusion, Melt Laying of Industrial Textiles

Polymer

Thermoplastic Polyurethane

Processing

Extrusion and Calander

Chemical structure

Polyether

Hardness

85A

Density

1,12 g/cm³

Form of delivery

Granules

Elongation at break

440 %

Tensile strength

30 MPa

Abrasion resistance

25 mm³

Applications

Conveyor belts

Polymer

Thermoplastic Polyurethane

Processing

Extrusion and Calander

Chemical structure

Aromatic polyethers

Hardness

91A

Density

1,12 g/cm³

Form of delivery

Granules

Elongation at break

450 %

Tensile strength

30 MPa

Abrasion resistance

25 mm³

Applications

Conveyor belts

Polymer

Thermoplastic Polyurethane

Processing

Extrusion and Calander

Chemical structure

Aromatic polyester

Hardness

92A

Density

1,22 g/cm³

Form of delivery

Granules

Elongation at break

490 %

Tensile strength

58,6 MPa

Applications

Coating for outdoor applications, e.g. inflatables, life jackets

Polymer

Aliphatic polyether-based TPU

Processing

Calandering, Extrusion

Hardness

A87

Density

1,08

Form of delivery

Granules

Processing conditions

160 - 170 °C

Elongation at break

390 %

Tensile strength

34 MPa